Yeah it’s good to have different opinions.
I can take some etches at various current levels to show you what I mean if you would be interested in seeing them.
It has been a while since I’ve done some with solid Mig wire etches but I’d expect to see less than 1mm of fusion at 200 amps on steel that thick.