those are not bad, you seem to have kept direction and those are fairly typical welds for fluxcore. I don't think you are welding on 5mm+-looks like 3mm from here.Surely this isn't normal? However cleaned up completely fine afterwards, it all just fell off...
Surely this isn't normal? However cleaned up completely fine afterwards, it all just fell off...
No, if you try welding a Gauloise butt end its bound to fall off . Leave the roundy bits till later -just stick with the flat bits for now, go on to fillet joints (or T JOINTS) next, when you get them right, you can have a go at roundy bits to flat bits as the angle is similar,its just the knack of going round the circle.