Im sorry @matt1978 you jave list me there with the time process ...if you mean twin torch .we have that..our lof is coming from the single...not alot of it .but enough to cause rework...we also have alot of gas slag...alot...so this should be looked at...we will have to have a look at the travel speeds again..maybe the wider but shallower arc deep in the half v that spray produces may also be beneficial ...i could see the need for looking at our libraries ...our stuff is being tested more stringent these days...our own welding guy set the parameters with igm first day...i wouldn't put my house on them..lol