this is a really strange problem as 95% or more of the welds are perfect and then one will bubble up and errupt as its cooling. I would be very grateful for any help.
we're plug welding spigots into mild steel scaffold tube
There doesn't seem to be any problem with gas supply or flow, we've tried changing to completely new tips, etc, etc but this really odd freak occurance keeps happening every 12-20 that are welded.
is it possible it could be a fault batch of wire?
we're plug welding spigots into mild steel scaffold tube
There doesn't seem to be any problem with gas supply or flow, we've tried changing to completely new tips, etc, etc but this really odd freak occurance keeps happening every 12-20 that are welded.
is it possible it could be a fault batch of wire?