Been playing today, trying to weld some thin mild plate, acording to my not so acurate plastic vernier 0.5mm, 1.6mm tungsten red, 8 lpm, amps down as low as it can go ( about 20 amps )
I can just about get a weld along the plate but not near the edge, trying to join 2 pieces it just keeps blowing the metal away.
I am soon to be hoping to be welding 0.8mm mild but hope its not going to blow that away, bot got any here to try at the moment.
So how thin can other people weld, am I doing something wrong or is it me just rubbish. My welds on around 2mm are quite good and got no problems there.