Hi..
I'm enjoying learning to tig weld, while I only get rare oppertunitys to practice I feel I'm improving, not very pretty but good and strong ..
However I always seem to get small holes in my welds even though I've tried to find a way of stopping it..
This work piece is steel, esab 160 dc tig set at 50 amps .. Stick out 2 mm everything cleaned inc rod with acetate.. Gas pure argon set at 6 ..
Welds are always a very dark colour too.. Not sure if this is the norm or not.
Thank you
I'm enjoying learning to tig weld, while I only get rare oppertunitys to practice I feel I'm improving, not very pretty but good and strong ..
However I always seem to get small holes in my welds even though I've tried to find a way of stopping it..
This work piece is steel, esab 160 dc tig set at 50 amps .. Stick out 2 mm everything cleaned inc rod with acetate.. Gas pure argon set at 6 ..
Welds are always a very dark colour too.. Not sure if this is the norm or not.