so i have been welding a few bits of ally lately and had some terrible results, (all goes black and pitted) and basically looks a totall mess with no real flow to the weld pool, with the exact same settings i moved onto a bit of flat sheet and ran a few beads perfectly fine
any ideas what could be causing this?
argon set at about 8lpm