gavuk
artful-bodger
- Messages
- 2,952
- Location
- Wilts
i think u should have used your own co2 .if its pure co2 and not nitrogen like the neighbours ,probably the cause of bad welds ,also 10Lpm is a good starting point ,too low gas will also cause problems with porosity......if using pub gas only pure co2 should be used