might depend on when some gents used it, it was hideous stuff for DIY use some years back I think, I know when I used it on my first MIG- a Clarke it was not brilliant.I've also had the impression, from things said here, that the quality of this stuff varies
I would normally use stick outdoors but I'll mostly be working on 1.5mm steel. Blowing holes all over the place would be a disaster.Wind breaks, higher flow rates, 6013 electrodes, try every thing you can before going gasless.
It looks like that's only available in larger spool sizes. I'd rather just get 1kg ...chances are I'd never have need of it again.Lincoln nr-211mp