Anyone seen a similar chart to this but in millimeters?

[BrokenBiker]

Interesting point you make about the box section/thermal mass, what if you could heat up the work piece first, say in an oven, do you think that would help?

Yes, preheat is a proven technique, although on such thing material I wouldn't think there is a much larger risk of distortion by preheating enough to make a difference...