I was wondering if anyone can give me some advice.
I would like to try flux core welding and was wondering if pure argon is the best to use, or is using a gas all that necessary ?
Secondly, will flux core wire say 0.9mm run ok in a standard wire liner or do I need to change the liner ?
Cheers chris
If digital appears to be the way forward, is it likely that control knobs will be phased out eventually ?
I have an sip dc tig and an r-tech mig 180, both good machines if you look after them.