Hi to all
I'm currently designing a lifting lug (made of ASTM A514) that is going to be welded (SMAW) on a truck body. However I'm not 100% if there is a major drawback when welding this metal to the truck body (Hardox 450). I calculated the preheat temperature and the required filler metal but not sure if this is enough.
I'm currently designing a lifting lug (made of ASTM A514) that is going to be welded (SMAW) on a truck body. However I'm not 100% if there is a major drawback when welding this metal to the truck body (Hardox 450). I calculated the preheat temperature and the required filler metal but not sure if this is enough.