The reason why I ask this is because I can always make the weld look decent on two passes. The root pass always looks terrible, but the second pass looks ok because the root pass gets swallowed up by the second pass. And if you're going vertical up, your material is at least 1/4 inch (6.35 millimeters) thick correct?