Richard.
Member
- Messages
- 18,347
- Location
- Cambridgeshire
Do you mean like little fuzzy growths rather than a ball?I use the 2% lanths purely because it means I don't have to keep different flavours from when I go from Stainless to Aluminium, also means I don''t have to wonder when I pick a tungsten out the drawer that the paint has rubbed off on as to what it is. They are not that much dearer than other flavours either but then I haven't bought the HFT ones and was considering trying some just to see if there was a difference or not.
@Richard. seeing as you are here, what is the normal cause for a tungsten getting nodules rather than balling, just crap tungstens or ?