See post above yours, brazing not being still used!Personally,i dont think brazing will hold that,not if its still being used,i'd rod it,my two bobs worth
brazing just a strong as a cold stitched nickel weld if not stronger.
Hot welded with nickel, yeah probably a higher tensile strength in the weld metal but I still think it would fail at a similar strength in the parent material.
It's a 50/50 process with nickel.I don’t even bother with nickel anymore
Totally agree. With nickel to work properly it’s got to be high grade iron which isn’t that oftenIt's a 50/50 process with nickel.
With brazing it's 100% guaranteed if done right.