I have a few bike panels with cracks in them, I have tried before at Plastic Welding but with little success.
What I have done in the past is use a soldering iron and melt the to parts together, never have felt strong, always brittle and tend to break after.
Is it just the technique I was using, I have been google'ing and would a Heat Gun and ABS rods be any different and work?
Cheers