I'm having problems with excessive penetration.
As I understand it that means too much heat.
I can't go any faster or I'll overtake the puddle. So I've turned the machine down by a couple of amps, but that's not helped.
Any thoughts from the experts?
(This is 2mm mild steel, lapweld, 64A +/-1A, 6lpm argon, 1.6mm for both rod and 2% Th Tungsten.)