I have started using T45, as it fits the bill. My problem is that I am brazing / bronze welding* it using TIG. Should I use a flux as well as argon, or does this defeat the object of using argon? Any tips doing this greatly appreciated.
on a related issue, what is the correct term? As far as I can tell, sticky the tubes together with brass is brazing, but is building up the fillets around the joint is bronze/brass welding?
on a related issue, what is the correct term? As far as I can tell, sticky the tubes together with brass is brazing, but is building up the fillets around the joint is bronze/brass welding?