Should not be a problem if it is reasonably thick & you use a small diameter rod, 1.6 or 2.0mm. MIG is far easier though with less chance of blowing holes through it.Bay dream said:Hello all, can anyone tell me if it is possible to use stick welding on structural repairs to a car's chassis.