yes......actually its my task to produce bad weldsbe a bad welder ?
yes...its my task actuallybe a bad welder ?
...
Chuck some oil on it before welding too.
yes......actually its my task to produce bad welds
Welcome aboard Abid Are you a teacher/lecturer, that you need to produce bad welds as examples to students?
i am a studentWelcome aboard Abid Are you a teacher/lecturer, that you need to produce bad welds as examples to students?
hahahahaAre we sure this question is genuine?. Never heard of any place called Pankistan, Maybe it should be Prankistan.
i am a student
Sir i just need to introduce porosity and in other to produce a crack.....If you can run 5mm rods, single with weave as you run it should be poor enough to be bad.
If you lip back over the edge of the weld pool where the slag is cooling as you advance, it should cause slag inclusions as well.
Better welds would be multi-pass with 3.2's or 4's in straight runs with little weave.
Sir i just need to introduce porosity and in other to produce a crack.....