aye most dinosaurs dont like a microprocessor changing volts w/s spatter like an explosion in a ball race factory with synergic i dare say twin pulse would be ok but we gettin good ndt results as is big butts 15 ft diam 46 mm thick 220 preheat 600 post weldPeople often don't know how to set the synergic machines, that's most of the issue. But those Millers do have a very nice arc to them.
My thoughts exactly.Shouldn't be much spatter at all with a pulse mig, that's kind of it's party piece.
I have always presumed that was the main features of the pulse.My thoughts exactly.
If it is set up properly spatter would be pretty much eliminated.
You wouldn't use a pulse with flux cored wire anyway. Basic or rutile.its a basic slag wire and is a totaly different ball game to rutile it bites like a filarc 88s rod and has very little slag
used similar stuff on big subsea structures for root runs on electrode negative on old oerlikon units with good results
I have as well.This is true, I have seen people try though