I was hoping that someone on here may be able to give me a little insight into neat little tight welds. Below are a couple of pictures of the sort of thing that i mean. Now these welds are very small and tight/neat etc but also very very flat. Now i can get consistant beading along a weld line but i have tried many setting/ combinations high amps moving fast/slow, lower amps fast slow to try and mimic that welds below and do you think i can.... no is the answer to that!!! I know once you have found that "prefect setting" is all about practice but just hoping someone could point me in the right direction.
i'm on about stainless steel 1-1.5mm thick just so you know.
Many thanks
i'm on about stainless steel 1-1.5mm thick just so you know.
Many thanks